Yttria ceramics: cutting tool application

The green compacts were sintered at 1600 in air for 2.5 h.

For an oxygen-deficient ceramic, a decrease of KIC was observed from 3.5 to 2.3 MPa m1/2.

The surface finish produced using yttria ceramic cutting tool is comparable to that of the commercial ZTA.

The yttria powders derived from yttrium hydroxide are calcined at 1100 jC with the sulfate ion doping to get transparent yttria.

Yttria is used as a sintering aid in sialons and silicon nitride

Richardson and Akinc reported that the yttrium oxide powders were isopressed and the relative unfired density of compacts was 49 % of theoretical density.

越詳細越好

謝謝!!!!!!!!!!!!

已更新項目:

不知道有沒有更好的翻譯

這是關於機械方面的

1 個解答

評分
  • 1 0 年前
    最佳解答

    Yttria ceramics: cutting tool application

    氧化釔窯業: 銳利的工具申請

    The green compacts were sintered at 1600 in air for 2.5 h.

    綠色的小型房車被泉華在 1600 在空氣中為 2.5 h。

    For an oxygen-deficient ceramic, a decrease of KIC was observed from 3.5 to 2.3 MPa m1/2.

    對於氧-不足的陶瓷,一個 KIC 的減少從 3.5 到 2.3 MPa m1/2 被觀察.

    The surface finish produced using yttria ceramic cutting tool is comparable to that of the commercial ZTA.

    使用氧化釔陶瓷的銳利工具的生產的表面的完成對商業 ZTA 的是可比較的。

    The yttria powders derived from yttrium hydroxide are calcined at 1100 jC with the sulfate ion doping to get transparent yttria.

    起源於的氧化釔粉釔氫氧化物在 1100 jC 被硫酸鹽離子攙雜所燒成石灰得到透明的氧化釔。

    Yttria is used as a sintering aid in sialons and silicon nitride

    氧化釔被使用當做一在 sialons 和矽氮化物中泉華幫助

    Richardson and Akinc reported that the yttrium oxide powders were isopressed and the relative unfired density of compacts was 49 % of theoretical density.

    理查森和 Akinc 報告釔氧化物粉是 isopressed ,而且不點燃小型房車的密度的親戚是 49% 理論上的密度。

    • Commenter avatar登入以對解答發表意見
還有問題?馬上發問,尋求解答。